Azzar b'liga baxxa Elettrodu manwali E8016-C4 Mod jack-up rigs Konsumabbli
Il-komponent ewlieni huwa 1.5% Ni, elettrodu tal-idejn tat-tip tal-potassju idroġenu baxx, f'temperatura operattiva -50C, it-toughness tal-impatt tal-metall depożitat hija eċċellenti
Ark stabbli, inqas splash, iffurmar tajjeb, tneħħija faċli tal-gagazza
Il-prestazzjoni tar-raġġi X hija eċċellenti.
KOMPONET KIMIKU:
LIGA (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Oħrajn | |
REGOLI GB/T | 0.082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - |
PROPRJETÀ MEKKANIKA:
PROPRJETÀ | QAĦA TA' RENDA (MPa) | QAWWA TA' ESTENSJONI (MPa) | Titwil (%) | VALUR IMATT J/℃ | Trattament bis-sħana °C*h | |||||
REGOLI GB/T | 505 | 600 | 23 | 105/-50 | 620*1 |
PARAMETRI RAKKOMANDATI TAL-WELJAR:
SPEĊIFIKAZZJONIJIET DJAMETRI (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
ELETTRIKU (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |
Sanmen Nuclear Power
-
JU2000E pjattaforma tat-tħaffir jack-up
Harbin elettriku tliet gate CMT
KOMPONET KIMIKU:
LIGA (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Oħrajn | |
REGOLI GB/T | 0.082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - |
PROPRJETÀ MEKKANIKA:
PROPRJETÀ | QAĦA TA' RENDA (MPa) | QAWWA TA' ESTENSJONI (MPa) | Titwil (%) | VALUR IMATT J/℃ | Trattament bis-sħana °C*h | |||||
REGOLI GB/T | 505 | 600 | 23 | 105/-50 | 620*1 |
PARAMETRI RAKKOMANDATI TAL-WELJAR:
SPEĊIFIKAZZJONIJIET DJAMETRI (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
ELETTRIKU (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |